Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.08 | 0.14 | ||
| Cr | 4.60 | 5.20 | ||
| Ni | - | remaining | ||
| Co | 6.00 | 8.00 | ||
| Mo | - | - | ||
| W | 15.30 | 16.50 | ||
| Al | 5.60 | 6.20 | ||
| Ti | 0.70 | 1.20 | ||
| Nb | 1.60 | 2.10 | ||
| Fe | - | 1.00 |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 818 (≥) | 114 (≥) | 23 | 11 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 539 (≥) | 948 (≥) | 24 | 22 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 431 | 482 | 787 |
We can customize the production of ЖC16K-BИ grade, contact us for the best solution.