Hot-Work Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.35 | 0.45 | ||
| Si | 0.80 | 1.20 | ||
| Mn | 0.20 | 0.50 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 4.75 | 5.50 | ||
| Mo | - | - | ||
| V | - | - | ||
| W | 4.00 | 5.25 | ||
| Ni＋Cu | - | 0.75 |
Hot-Work Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 346 (≥) | 857 (≥) | 24 | 43 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 448 (≥) | 511 (≥) | 23 | 43 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 241 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 535 | 152 | 334 |
We can customize the production of H14 grade, contact us for the best solution.