Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.14 | 0.18 | ||
| Si | - | 0.60 | ||
| Mn | - | 0.60 | ||
| P | - | 0.030 | ||
| S | - | 0.025 | ||
| Cr | 10.50 | 12.00 | ||
| Ni | 1.40 | 1.80 | ||
| Mo | 0.35 | 0.50 | ||
| W | 1.60 | 2.00 | ||
| Ti | - | 0.20 | ||
| V | 0.18 | 0.30 |
Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 428 (≥) | 561 (≥) | 11 | 34 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 224 (≥) | 192 (≥) | 31 | 23 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 875 | 525 | 575 |
We can customize the production of 16X11H282MΦ grade, contact us for the best solution.