Russia TY standard grades and chemical compositions of the high temperature alloy castings
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.02 | 0.10 | ||
| Cr | 30.00 | 35.00 | ||
| Al | 1.00 | 1.60 | ||
| Mo | 2.90 | 3.50 | ||
| Ti | 0.70 | 1.30 | ||
| Co | 0.20 | 0.80 | ||
| W | 4.70 | 5.30 | ||
| Ni | - | remaining | ||
| Nb | 0.70 | 5.30 | ||
| Fe | - | 6.00 | ||
| B | - | 0.005 | ||
| Ce | - | 0.03 | ||
| V | - | - | ||
| Zr | - | - | ||
| Mn | - | 0.50 | ||
| Si | - | 0.40 | ||
| S | - | 0.010 | ||
| P | - | 0.015 | ||
| Y | - | 0.04 | ||
| Ca | - | 0.02 |
Russia TY standard grades and chemical compositions of the high temperature alloy castings
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 523 (≥) | 341 (≥) | 21 | 13 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 442 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 896 (≥) | 189 (≥) | 24 | 11 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 579 | 589 | 869 |
We can customize the production of BX9Л grade, contact us for the best solution.