Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Si | - | 0.60 | ||
| Mn | - | 0.50 | ||
| P | - | 0.015 | ||
| S | - | 0.010 | ||
| Cr | 13.00 | 16.00 | ||
| Ni | - | remaining | ||
| Mo | 2.00 | 4.00 | ||
| Al | 1.70 | 2.30 | ||
| Ti | 1.80 | 2.30 | ||
| Fe | - | 5.00 | ||
| W | 5.00 | 7.00 | ||
| B | - | 0.020 | ||
| V | - | 0.50 | ||
| Ce | - | 0.02 |
Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 575 (≥) | 273 (≥) | 31 | 22 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 765 (≥) | 245 (≥) | 41 | 34 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 394 | 947 | 112 |
We can customize the production of XH70BMTЮ grade, contact us for the best solution.