Carbon Wolfram Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 1.20 | 1.40 | ||
| Si | 0.10 | 0.50 | ||
| Mn | 0.10 | 0.50 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 0.20 | 0.40 | ||
| Mo | - | - | ||
| V | - | - | ||
| W | - | - | ||
| Ni＋Cu | - | 0.75 |
Carbon Wolfram Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 135 (≥) | 183 (≥) | 31 | 14 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 225 (≥) | 464 (≥) | 43 | 32 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 425 | 134 | 385 |
We can customize the production of F2 grade, contact us for the best solution.