Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Si | 0.50 | 1.00 | ||
| Mn | 1.00 | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.020 | ||
| Cr | 18.50 | 20.50 | ||
| Ni | 10.00 | 13.00 | ||
| Mo | - | 0.30 | ||
| Nb | 0.80 | 1.10 | ||
| V | 1.00 | 1.30 | ||
| N | 0.10 | 0.20 |
Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 693 (≥) | 252 (≥) | 14 | 34 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 346 (≥) | 786 (≥) | 44 | 24 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 241 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 834 | 716 | 154 |
We can customize the production of 08X19H12TΦ grade, contact us for the best solution.