Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.22 | ||
| Si | - | 0.40 | ||
| Mn | - | 0.75 | ||
| P | - | - | ||
| S | - | - | ||
| Ni | - | 0.75 | ||
| Cr | - | 12.50 | ||
| Al | - | - | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | remaining | ||
| N | - | - | ||
| Mo | - | 1.00 | ||
| W | - | 1.00 | ||
| V | - | 0.22 |
Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 568 (≥) | 641 (≥) | 44 | 21 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 673 (≥) | 996 (≥) | 11 | 43 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 198 | 226 | 528 |
We can customize the production of A 352 J42215 grade, contact us for the best solution.