Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.01 | ||
| Si | - | 0.05 | ||
| Mn | - | 1.50 | ||
| P | - | 0.04 | ||
| S | - | 0.01 | ||
| Ni | - | remaining | ||
| Cr | 0.50 | 1.50 | ||
| Al | 0.10 | 0.50 | ||
| Cu | - | 0.50 | ||
| Ti | - | - | ||
| Fe | 1.00 | 6.00 | ||
| Mo | 26.00 | 30.00 | ||
| Co | - | 2.50 |
Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 918 (≥) | 586 (≥) | 43 | 11 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 341 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 574 (≥) | 294 (≥) | 23 | 24 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 252 | 492 | 458 |
We can customize the production of B 446 N06219 grade, contact us for the best solution.