Nickel-Chromium-Molybdenum-Columbium Alloys (UNS N06625 and UNS N06852) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Pipe and Tube
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.01 | ||
| Si | - | 0.05 | ||
| Mn | - | 1.50 | ||
| P | - | 0.04 | ||
| S | - | 0.01 | ||
| Ni | - | remaining | ||
| Cr | 0.50 | 1.50 | ||
| Al | 0.10 | 0.50 | ||
| Cu | - | 0.50 | ||
| Ti | - | - | ||
| Fe | 1.00 | 6.00 | ||
| Mo | 26.00 | 30.00 | ||
| Co | - | 2.50 |
Nickel-Chromium-Molybdenum-Columbium Alloys (UNS N06625 and UNS N06852) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Pipe and Tube
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 793 (≥) | 953 (≥) | 24 | 41 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 113 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 353 (≥) | 127 (≥) | 42 | 33 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 979 | 399 | 937 |
We can customize the production of SB-444 N06219 grade, contact us for the best solution.