Nickel-iron-chromium-molybdenum-copper low-carbon alloys bar and wire
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Si | - | 0.30 | ||
| Mn | - | 0.80 | ||
| Cr | - | 19.00 | ||
| Ni | - | 14.00 | ||
| Mo | - | - | ||
| Co | - | - | ||
| W | - | - | ||
| Al | - | - | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | remaining | ||
| Nb | - | 1.60 |
Nickel-iron-chromium-molybdenum-copper low-carbon alloys bar and wire
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 653 (≥) | 546 (≥) | 12 | 41 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 729 (≥) | 538 (≥) | 11 | 21 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 977 | 363 | 436 |
We can customize the production of B 649 R20033 grade, contact us for the best solution.