PH13-8Mo, 1.4534, Alloy 13-8 Stainless Steels to SAE AMS 5840E (2010)

PH13-8Mo, 1.4534, Alloy 13-8 - Specification & Application

  • SAE AMS 5840E (2010) - Steel, Corrosion and Heat Resistant, Welding Wire 13Cr - 8.0Ni - 2.3Mo - 1.1Al Vacuum Melted
  • ASTM A564-2019 - XM-13
  • ASTM A693 - PH13-8Mo

Steel, Corrosion and Heat Resistant, Welding Wire 13Cr - 8.0Ni - 2.3Mo - 1.1Al Vacuum Melted

Chemical composition(wt.%) of PH13-8Mo, 1.4534, Alloy 13-8 grade: to SAE AMS 5840E (2010)

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.05
Si - -
Mn - -
Cr 12.25 13.25
Ni 7.50 8.50
Mo 2.00 2.50
Co - -
W - -
Al 0.90 1.35
Cu - -
Ti - -
Fe - -

Mechanical properties of grade PH13-8Mo, 1.4534, Alloy 13-8 grade: to SAE AMS 5840E (2010)

Yield Strength,Rp 0.2(MPa)

Condition Min Max Similar Note
H950 1415

Tensile Strength,Rm(MPa)

Condition Min Max Similar Note
H950 1515

Impact,Kv/Ku(J)

Condition Min Max Similar Note

Elongation,A(%)

Condition Min Max Similar Note
H950 10%

Reduction of area,(%)

Condition Min Max Similar Note

Hardness

Condition Type Min Max Similar Note
H950 HRC 45
H950 HB 450

Related properties

+A - HRC - 38
A - HB - 363
H950 - Tensile strength, Rm 1515 MPa
H950 - Yield point, Re 1415 MPa
H950 - Elongation, A 10%
H950 - HRC 45
H950 - HB 450
H1000 - Tensile strength, Rm 1415 MPa
H1000 - Yield point, Re 1310 MPa
H1000 - Elongation, A 10%
H1000 - HRC 43
H1000 - HB 400

PH13-8Mo, 1.4534, Alloy 13-8 - Detail

Chromium-nickel-molybdenum stainless construction steel with aluminum additive X3CrNiMoAl13-8-2, 1.4534, PH13-8 Mo, 13-8 Mo precipitation strengthened for use in the aerospace, petroleum and petrochemical industries.