00Cr18Ni14Mo2Cu2 0Cr18Ni12Mo2Cu ultra-low carbon steel, stainless steel 00Cr18Ni14Mo2Cu2 stainless steel is better than 0Cr18Ni12Mo2Cu2 resistance to intergranular corrosion.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.030 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.030 | ||
| Ni | 12.00 | 16.00 | ||
| Cr | 17.00 | 19.00 | ||
| Mo | 1.20 | 2.75 | ||
| Cu | 1.00 | 2.50 |
00Cr18Ni14Mo2Cu2
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 683 (≥) | 392 (≥) | 11 | 21 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 214 (≥) | 337 (≥) | 13 | 12 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 321 | 673 | 741 |
We can customize the production of 00Cr18Ni14Mo2Cu2 grade, contact us for the best solution.