Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | 8.50 | 12.00 | ||
| P | - | 0.060 | ||
| S | - | 0.030 | ||
| Ni | 4.00 | 6.00 | ||
| Cr | 17.00 | 19.00 | ||
| Mo | 2.8 | 3.5 | ||
| N | 0.20 | 0.30 |
1Cr18Mn10Ni5Mo3N Stainless Steel Bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 328 (≥) | 756 (≥) | 42 | 32 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 442 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 956 (≥) | 767 (≥) | 13 | 23 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 364 | 843 | 681 |
We can customize the production of 1Cr18Mn10Ni5Mo3N grade, contact us for the best solution.