Martensitic Stainless Steel Bars for High-Temperature Service
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.15 | 0.20 | ||
| Mn | - | 0.50 | ||
| Si | - | 0.50 | ||
| P | - | 0.04 | ||
| S | - | 0.03 | ||
| Cr | 12.00 | 14.00 | ||
| Ni | 1.80 | 2.20 | ||
| Mo | - | - | ||
| W | 2.50 | 3.50 |
Martensitic Stainless Steel Bars for High-Temperature Service
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 882 (≥) | 977 (≥) | 44 | 42 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 138 (≥) | 273 (≥) | 34 | 32 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 992 | 958 | 666 |
We can customize the production of A 565 S41800 grade, contact us for the best solution.