A 565 S42200 Stainless Steels to A 565/A 565M (2010)

A 565 S42200 - Specification & Application

  • A 565/A 565M (2010) - Martensitic Stainless Steel Bars for High-Temperature Service

Martensitic Stainless Steel Bars for High-Temperature Service

Chemical composition(wt.%) of A 565 S42200 grade: to A 565/A 565M (2010)

Elements Min.(≥) Max.(≤) Similar Remarks
C 0.20 0.25
Mn - 1.00
Si - 0.75
P - 0.04
S - 0.03
Cr 11.50 13.50
Ni 0.50 1.00
Mo 0.75 1.25
V 0.15 0.30
W 0.75 1.25

A 565 S42200 - Detail

Martensitic Stainless Steel Bars for High-Temperature Service

Mechanical properties of grade A 565 S42200 A 565/A 565M (2010)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
693 (≥) 682 (≥) 43 34 14 Solution and Aging, Annealing, Ausaging, Q+T,etc 231

Physical properties of grade A 565 S42200 A 565/A 565M (2010)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
738 (≥) 836 (≥) 12 44 42 Solution and Aging, Annealing, Ausaging, Q+T,etc 241
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
417 869 586
We can customize the production of A 565 S42200 grade, contact us for the best solution.