wrought steels used in aeronautical constructions
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.77 | 0.85 | ||
| Si | - | 0.25 | ||
| Mn | - | 0.35 | ||
| P | - | 0.025 | ||
| S | - | 0.015 | ||
| Cr | 3.25 | 4.25 | ||
| Ni | - | 0.10 | ||
| Mo | 4.00 | 5.00 | ||
| V | 0.90 | 1.10 | ||
| W | - | 0.25 | ||
| Co | - | 0.25 |
E80DCV40 Air 9160C wrought steels used in aeronautical constructions
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 422 (≥) | 589 (≥) | 14 | 21 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 343 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 791 (≥) | 222 (≥) | 23 | 12 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 678 | 834 | 524 |
We can customize the production of E80DCV40 Air 9160/C grade, contact us for the best solution.