Classification and designation for superalloys and high temperature intermetallic materials
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.07 | ||
| Cr | 19.0 | 22.0 | ||
| Ni | - | Remainder | ||
| Al | 0.70 | 1.20 | ||
| Nb | 1.15 | 1.65 | ||
| Ti | 2.50 | 3.00 | ||
| Fe | - | 1.5 | ||
| Si | - | 0.65 | ||
| Mn | - | 0.35 | ||
| P | - | 0.015 | ||
| S | - | 0.007 | ||
| B | - | 0.01 | ||
| Ce | - | 0.01 |
GH4133
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 133 (≥) | 686 (≥) | 31 | 12 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 267 (≥) | 254 (≥) | 32 | 41 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 759 | 213 | 262 |
We can customize the production of GH4133 grade, contact us for the best solution.