Engine poppet valve information report
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.47 | 0.55 | ||
| Si | 1.00 | 2.00 | ||
| Mn | - | 0.60 | ||
| Cr | 7.50 | 9.50 | ||
| Ni | - | 0.60 | ||
| Mo | - | - | ||
| Co | - | - | ||
| W | - | - | ||
| Al | - | - | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | - | ||
| P | - | 0.03 | ||
| S | - | 0.03 |
Engine poppet valve information report
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 646 (≥) | 791 (≥) | 12 | 21 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 546 (≥) | 819 (≥) | 23 | 31 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 992 | 294 | 949 |
We can customize the production of SUH 11M grade, contact us for the best solution.