Austenitic Chromium Nickel Silicon Heat Resisting Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.20 | ||
| Mn | - | 0.80 | ||
| Si | - | 3.50 | ||
| P | - | - | ||
| S | - | - | ||
| Cr | - | 18.50 | ||
| Ni | - | 14.50 | ||
| Mo | - | - | ||
| Al | - | 1.00 | ||
| N | 0.14 | 0.20 |
Austenitic Chromium Nickel Silicon Heat Resisting Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 263 (≥) | 246 (≥) | 32 | 23 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 389 (≥) | 461 (≥) | 13 | 13 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 343 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 698 | 971 | 621 |
We can customize the production of S30615 grade, contact us for the best solution.