Hot-Work Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.45 | 0.55 | ||
| Si | 0.15 | 0.40 | ||
| Mn | 0.15 | 0.40 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 3.75 | 4.50 | ||
| Mo | - | - | ||
| V | 0.75 | 1.25 | ||
| W | 17.25 | 19.00 | ||
| Ni＋Cu | - | 0.75 |
Hot-Work Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 677 (≥) | 429 (≥) | 43 | 13 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 293 (≥) | 344 (≥) | 41 | 12 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 143 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 174 | 276 | 135 |