Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| Si | - | 0.40 | ||
| Mn | - | 0.40 | ||
| P | - | 0.015 | ||
| S | - | 0.010 | ||
| B | - | 0.02 | ||
| Ce | - | 0.015 | ||
| Zr | - | 0.02 | ||
| Y | - | 0.03 | ||
| Pb | - | - | ||
| Bi | - | - | ||
| V | 0.05 | 0.10 | ||
| La | - | 0.005 | ||
| Hf | 0.30 | 1.20 | ||
| Ca | - | 0.005 |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 634 (≥) | 874 (≥) | 11 | 41 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 343 (≥) | 247 (≥) | 44 | 11 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 923 | 614 | 351 |
We can customize the production of ЖC30-BИ grade, contact us for the best solution.