Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Mn | - | 0.20 | ||
| Si | - | 1.00 | ||
| P | - | 0.01 | ||
| S | - | 0.008 | ||
| Cr | 12.25 | 13.00 | ||
| Ni | 7.50 | 8.50 | ||
| Mo | 2.00 | 2.50 | ||
| Al | 0.90 | 1.35 | ||
| N | - | 0.01 |
Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 942 (≥) | 879 (≥) | 41 | 43 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 188 (≥) | 811 (≥) | 11 | 33 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 122 | 148 | 542 |
We can customize the production of S13800 grade, contact us for the best solution.