Iron and steel. Stainless steel for high temperature application
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.040 | ||
| Si | - | 0.75 | ||
| Mn | - | 0.08 | ||
| P | - | 0.030 | ||
| S | - | 0.015 | ||
| Cr | 16.00 | 18.00 | ||
| Mo | - | - | ||
| Ni | - | - | ||
| Ti | 4×(C+N)+0.20 | 0.75 |
Iron and steel. Stainless steel for high temperature application
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 919 (≥) | 889 (≥) | 41 | 42 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 666 (≥) | 197 (≥) | 33 | 13 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 297 | 199 | 611 |
We can customize the production of Z4CT17 grade, contact us for the best solution.