Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.16 | 0.24 | ||
| Si | 3.20 | 4.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.03 | ||
| S | - | 0.03 | ||
| Cr | 17.0 | 19.5 | ||
| Ni | 13.5 | 16.0 | ||
| Al | 0.80 | 1.50 |
Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 377 (≥) | 321 (≥) | 42 | 24 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 138 (≥) | 817 (≥) | 34 | 33 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 694 | 359 | 549 |