AISI 414

AISI 414 Special Alloy

Chemical composition%of the ladle analysis of gradeAISI 414

C(％)	Si(％)	Mn(％)	P(％)	S(％)	Cr(％)	Ni(％)
0.15	1.00	1.00	0.04	0.03	11.5-13.5	1.25-2.50

AISI Type 414 is a Martensitic Standard grade Stainless Steel. It is commonly called AISI Type 414 Chromium steel. It is composed of (in weight percentage) 0.15% Carbon (C), 1.00% Manganese (Mn), 1.00% Silicon (Si), 11.5-13.5% Chromium (Cr), 1.25-2.50% Nickel (Ni), 0.04% Phosphorus (P), 0.03% Sulfur (S), and the base metal Iron (Fe). Other designations of AISI Type 414 stainless steel include UNS S41400 and AISI 414.

Steel is the common name for a large family of iron alloys. Steels can either be cast directly to shape, or into ingots which are reheated and hot worked into a wrought shape by forging, extrusion, rolling, or other processes. Wrought steels are the most common engineering material used, and come in a variety of forms with different finishes and properties. Stainless steels are high-alloy steels that have superior corrosion resistance than other steels because they contain large amounts of chromium. Stainless steels contains at least 10% chromium, with or without other elements. Stainless steels can be divided into three basic groups based on their crystalline structure: austenitic, ferritic, and martensitic.
The typical elastic modulus of stainless steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of stainless steels ranges from 7.75 to 8.1 g/cm3. The typical tensile strength varies between 515 and 827 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions.

Mechanical properties of gradeAISI 414

Proof strength R_p0.2(MPa)	Tensile strength R_m(MPa)	Impact energy KV(J)	Elongation at fracture A(%)	Reduction in cross section on fracture Z(%)	As-Heat-Treated Condition	Brinell hardness(HBW)
557(≥)	788(≥)	33	23	21	Solution and Aging,Annealing,Ausaging,Q+T,etc	342

Physical properties of grade AISI 414

Property	Density kg/dm3	Temperature T °C/F	Specific heat J/kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2
474(≥)	924(≥)	14	11	14	Solution and Aging,Annealing,Ausaging,Q+T,etc	343
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0)N/mm2	Creep rupture strength (10000h) (Rp1,0)N/mm2
186	624	854

AISI 414 Range of products


Product type	Products	Dimension	Processes	Deliver Status
Plates/Sheets	Plates/Sheets	0.08-200mm(T)WL	Forging,hot rolling and cold rolling	Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Steel Bar	Round Bar,Flat Bar,Square Bar	Φ8-1200mm*L	Forging,hot rolling and cold rolling,Cast	Black,Rough Turning,Shot Blasting,
Coil/Strip	Steel Coil/Steel Strip	0.03-16.0x1200mm	Cold-Rolled&Hot-Rolled	Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Pipes/Tubes	Seamless Pipes/Tubes,Welded Pipes/Tubes	OD:6-219mm x WT:0.5-20.0mm	Hot extrusion,Cold Drawn,Welded	Annealed,Solution and Aging,Q+T,ACID-WASHED

Equivalent Grade

1 1.2414 2 UNS S41425 3 UNS S41425 4 SAE NV7(4140) 5 UNS H41400 6 ICI 4140 7 414100 8 414109 9 414120 10 414140 11 GH4141 12 GH4145 13 GH4146 14 A 276 S41400 15 A 314 S41400 16 A 473 S41400 17 A 580 S41400 18 S41400 19 A 276 S41425 20 A 314 S41425

Equivalent Products

1 4145H Hollow Bar