Austenitic Chromium Manganese Stainless Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Mn | 14.50 | 16.00 | ||
| Si | 0.30 | 1.00 | ||
| P | - | 0.045 | ||
| S | - | 0.03 | ||
| Cr | 17.00 | 18.50 | ||
| Ni | - | 0.75 | ||
| Mo | - | - | ||
| N | - | 0.35 |
Austenitic Chromium Manganese Stainless Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 867 (≥) | 811 (≥) | 22 | 24 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 423 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 771 (≥) | 936 (≥) | 22 | 44 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 154 | 639 | 796 |
We can customize the production of S21400 grade, contact us for the best solution.