An age-hardened alloy that combines the excellent corrosion resistance characteristics of Nickel 200 with the added advantages of greater strength and hardness.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| Ni | 93.0 | - | ||
| Cu | - | 0.25 | ||
| Si | - | 1.00 | ||
| Mn | - | 0.50 | ||
| Fe | - | 0.60 | ||
| S | - | 0.01 | ||
| Ti | 0.25 | 1.00 | ||
| C | - | 0.30 | ||
| Al | 4.00 | 4.75 |
An age-hardened alloy that combines the excellent corrosion resistance characteristics of Nickel 200 with the added advantages of greater strength and hardness. The alloy is used for springs requiring high electrical conductivity, parts of equipment requiring good thermal conductivity and magnetostrictive units, which are operated under stress conditions in which the fatigue strength of Nickel 200 is inadequate.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 216 (≥) | 226 (≥) | 44 | 23 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 614 (≥) | 877 (≥) | 13 | 23 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 334 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 217 | 417 | 217 |
We can customize the production of ALLOY 301 grade, contact us for the best solution.