Alloyed WCrV steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.75 | 0.85 | ||
| Si | 0.40 | 0.60 | ||
| Mn | 0.30 | 0.50 | ||
| P | - | 0.035 | ||
| S | - | 0.035 | ||
| Cr | 1.00 | 1.20 | ||
| Mo | - | - | ||
| V | 0.25 | 0.35 | ||
| W | 1.80 | 2.10 |
Alloyed WCrV steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 485 (≥) | 276 (≥) | 21 | 24 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 993 (≥) | 276 (≥) | 44 | 42 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 564 | 873 | 758 |
We can customize the production of 1.2552 grade, contact us for the best solution.