Mainly used for cold working mold: gauge, die for thread rolling, cutting tool for metal, forming roll, die for press.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 1.4 | 1.6 | ||
| Si | - | 0.4 | ||
| Mn | - | 0.6 | ||
| P | - | 0.03 | ||
| S | - | 0.03 | ||
| Cr | 11 | 13 | ||
| Mo | 0.8 | 1.2 | ||
| V | 0.2 | 0.5 |
The steel is a widely used international air cooling hardening cold work die steel.Approved by electric furnace smelting and the electroslag solubility, high purity, better toughness, uniform organization, has good high temperature strength, toughness and resistance to high temperature fatigue performance, can withstand the temperature shock.
High hardness, high wear resistant uniform eutectic carbides, good toughness, not easy craze, > 62 HRC hardness after quenching.At 525 ℃ nitriding processing time for 20 h/h/h, 60 ammoniation layer depth of 0.25 mm / 0. 30 mm / 0. 35 mm, the surface hardness is 1250 hv,At 570 ℃ nitriding processing time is 2 h, nitriding depth 10 ~ 20 microns, the surface hardness is 950 hv.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 636 (≥) | 954 (≥) | 13 | 12 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 621 (≥) | 496 (≥) | 33 | 42 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 193 | 749 | 974 |
We can customize the production of SKD-11 grade, contact us for the best solution.