Steel, Bars and Forgings 2.0Cr - 10Ni - 14Co - 1.0Mo (0.15 - 0.19C) Vacuum Melted, Normalized and Overaged
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.13 | 0.17 | ||
| Si | - | 0.10 | ||
| Mn | - | 0.10 | ||
| P | - | 0.008 | ||
| S | - | 0.005 | ||
| Ni | 9.50 | 10.50 | ||
| Cr | 1.80 | 2.20 | ||
| Al | - | 0.015 | ||
| Cu | - | - | ||
| Ti | - | 0.015 | ||
| Fe | - | - | ||
| N | - | 0.0015 | ||
| Mo | 0.90 | 1.10 | ||
| W | - | - | ||
| O | - | 0.0015 | ||
| Co | 13.50 | 14.50 |
Steel, Bars and Forgings 2.0Cr - 10Ni - 14Co - 1.0Mo (0.15 - 0.19C) Vacuum Melted, Normalized and Overaged
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 263 (≥) | 871 (≥) | 13 | 44 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 332 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 711 (≥) | 462 (≥) | 32 | 21 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 198 | 519 | 838 |
We can customize the production of AF 1410 grade, contact us for the best solution.