Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.10 | 0.17 | ||
| Cr | 15.00 | 17.00 | ||
| Ni | - | remaining | ||
| Co | - | - | ||
| Mo | 3.50 | 5.00 | ||
| W | 2.00 | 2.50 | ||
| Al | 2.00 | 2.80 | ||
| Ti | 2.00 | 3.00 | ||
| Nb | - | - | ||
| Fe | 6.00 | 7.50 |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 698 (≥) | 499 (≥) | 31 | 43 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 622 (≥) | 891 (≥) | 34 | 14 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 344 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 175 | 118 | 527 |
We can customize the production of BЖЛ1-BИ grade, contact us for the best solution.