MARAGING (C) 300

MARAGING (C) 300 Special Alloy

Chemical composition%of the ladle analysis of gradeMARAGING (C) 300

C(％)	Si(％)	Mn(％)	P(％)	S(％)	Cr(％)	Ni(％)	Mo(％)	Cu(%)	Co(%)	Al(%)	Ti(%)	Other(%)
0.03	0.10	0.10	0.010	0.010	0.50	18.00-19.00	4.60-5.20	0.50	8.50-9.50	0.05-0.15	0.50 -0.80	Fe Bal

AMS 6514

MARAGING (C) 300
General: Maraging is a 18% nickel, cobalt strengthened steel (C-type), with excellent mechanical properties, workability and heat
treatment characteristics.
Applications:  Typical applications for maraging include missile and rocket motor cases, landing and takeoff gear, munitions,
aerospace, extrusion tooling, die casting, high performance shafting, gears and fasteners

Material Melt Method: Maraging melt method is a VIM (Vacuum Induction Melt) + VAR (Vacuum Arc Remelt)
As Shipped Condition: Maraging is supplied in the annealed and descaled condition. The alloy is very tough, relatively soft (36
Rc Max.), therefore, readily machined and formed.
*Bar Tolerances:  .250” - .499” .500” - .999” 1.000” – 3.625” 3.626” – 6.000” 6.001” – 8.000” 8.001” – 10.000”
-.000/+.005 -.000/+.010 -.000/+.031 -.000/+.047 -.000/+.063 -.000/+0.078
Minimum Properties after Aging:
Hardness ……………… 52 Rc Charpy V-notch ……… 12 ft/lbs. min  Reduction of Area ……. 47%
Elongation ……………. 5.0%  Yield Strength …………. 280 ksi Fracture Toughness ….. 60
Physical Properties:
Density………………………………… .289 lbs./cu. In
Average Coefficient of Thermal Expansion (70 – 900 F) ……………… 5.6 x 10 -6 in/in. F
Heat Treatment Aging Process: (Non Die Casting Applications)
Material is to be heat treated to 900 F +/- 10 holding at temperature for 6 hours then cooling at room air temperature. During the aging
treatment maraging shrinks uniformly and predictably on all dimensions .001 in/in
Heat Treatment Aging Process: (Die Casting Applications)
Following the rough machining of the die, anneal at 1500-1525 F for 1 hour per inch of thickness is recommended. After finish
machining , an aging heat treatment of 980-1000 F for 6 hours is recommended.
Machining:
Maraging steel in the annealed condition is comparable to 4340. However, when maraging is aged, the type of cutting tool and speeds
change. Rigid equipment, firm tool supports, sharp tools and abundant coolant are essential.
Welding:
Maraging is weld able without preheat, in both the annealed and aged condition. Only an aging heat treatment is needed to restore in the
weld.
Standards:
AMS 6514 ASTM A 538 *Mil-S-46850D UNS K93120
*DMI product is not supplied to the dimensional tolerances of MIL-S-46850D.
*The information, data and specifications presented here are representative only, and are not guaranteed values. Material or products
applications described are solely for illustrative purposes and should not be construed as express or implied warranties for fitness for these
or other applications

Mechanical properties of gradeMARAGING (C) 300

Proof strength Rp0.2(MPa)	Tensile strength Rm(MPa)	Impact energy KV(J)	Elongation at fracture A(%)	Reduction in cross section on fracture Z(%)	As-Heat-Treated Condition	Brinell hardness(HBW)
638(≥)	223(≥)	22	14	42	Solution and Aging,Annealing,Ausaging,Q+T,etc	424

Physical properties of grade MARAGING (C) 300

Property	Density kg/dm3	Temperature T °C/F	Specific heat J/kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2	Expansion rate
874(≥)	561(≥)	31	41	22	Solution and Aging,Annealing,Ausaging,Q+T,etc	332
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0)N/mm2	Creep rupture strength (10000h) (Rp1,0)N/mm2
334	752	462

MARAGING (C) 300 Range of products

Product type	Products	Dimension	Processes	Deliver Status
Plates/Sheets	Plates/Sheets	0.08-200mm(T)*W*L	Forging,hot rolling and cold rolling	Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Steel Bar	Round Bar,Flat Bar,Square Bar	Φ8-1200mm*L	Forging,hot rolling and cold rolling,Cast	Black,Rough Turning,Shot Blasting,
Coil/Strip	Steel Coil/Steel Strip	0.03-16.0x1200mm	Cold-Rolled&Hot-Rolled	Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Pipes/Tubes	Seamless Pipes/Tubes,Welded Pipes/Tubes	OD:6-219mm x WT:0.5-20.0mm	Hot extrusion,Cold Drawn,Welded	Annealed,Solution and Aging,Q+T,ACID-WASHED