Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.06 | 0.11 | ||
| Cr | 11.00 | 12.50 | ||
| Ni | - | remaining | ||
| Co | 8.00 | 10.00 | ||
| Mo | 3.80 | 4.50 | ||
| W | 3.80 | 4.50 | ||
| Al | 4.00 | 4.80 | ||
| Ti | 2.50 | 3.20 | ||
| Nb | - | - | ||
| Fe | - | 2.00 |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 727 (≥) | 367 (≥) | 11 | 34 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 947 (≥) | 261 (≥) | 41 | 23 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 684 | 434 | 844 |
We can customize the production of ЖC3ЛK-BИ grade, contact us for the best solution.