Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.200 | ||
| S | - | 0.150 | ||
| Ni | 8.00 | 10.00 | ||
| Cr | 17.00 | 19.00 |
Y1Cr18Ni9
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 223 (≥) | 443 (≥) | 44 | 43 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 618 (≥) | 515 (≥) | 12 | 41 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 143 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 914 | 815 | 185 |
We can customize the production of Y1Cr18Ni9 grade, contact us for the best solution.