Iron and steel. Stainless steel for general purposes. Semi- finished products, bars and wire rod
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.080 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.50 | ||
| P | - | 0.040 | ||
| S | 0.15 | 0.35 | ||
| Cr | 16.00 | 18.00 | ||
| Mo | 0.20 | 0.60 | ||
| Ni | - | 0.75 |
Iron and steel. Stainless steel for general purposes. Semi- finished products, bars and wire rod
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 911 (≥) | 696 (≥) | 23 | 34 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 738 (≥) | 516 (≥) | 42 | 42 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 439 | 878 | 822 |
We can customize the production of Z8CF17 grade, contact us for the best solution.