Austenitic Chromium Manganese Nickel Stainless Steel, Low carbon
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.04 | ||
| Mn | 8.00 | 10.00 | ||
| Si | - | 1.00 | ||
| P | - | 0.06 | ||
| S | - | 0.03 | ||
| Cr | 19.00 | 21.50 | ||
| Ni | 5.50 | 7.50 | ||
| Mo | - | - | ||
| N | 0.15 | 0.40 |
Austenitic Chromium Manganese Nickel Stainless Steel, Low carbon
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 892 (≥) | 678 (≥) | 31 | 21 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 653 (≥) | 998 (≥) | 23 | 23 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 434 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 463 | 624 | 849 |