NICKEL 201

NICKEL 201 Superalloys to UNS N02201

NICKEL 201 - Specification & Application

• UNS N02201 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• ASME Code Case 2249 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• BS 3072 – 3074 (NA12) - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• ASTM B 160 – B 163, B 366,B 725, B 730, B 751,B 775, B 829 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• DIN 17740, 17750 – 17754 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• ASME SB-160 – SB-163,SB-366, SB-725, SB-730,SB-751, SB-775, SB-829 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.
• ISO 6207, 6208, 9723 – 9725 - Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.

Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.

Chemical composition(wt.%) of NICKEL 201 grade: to UNS N02201

NICKEL 201 - Detail

Commercially pure (99.6%) wrought nickel essentially the same as Nickel 200 but with a lower carbon content to prevent embrittlement by intergranular carbon at temperatures over 600°F (315°C). Lower carbon content also reduces hardness, making Nickel 201 particularly suitable for cold-formed items.

STANDARD PRODUCT FORMS

Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.

PHYSICAL CONSTANTS AND THERMAL PROPERTIES

Density, Ib/in3........................................................................0.321
g/cm3......................................................................... 8.89
Melting Range, °F ...................................................2615 – 2635
°C ...................................................1435 – 1446
Specific Heat, Btu/lb•°F ....................................................0.109
J/kg•°C........................................................... 456
Curie Temperature, °F ........................................................... 680
°C ........................................................... 360
Permeability ........................................................ Ferromagnetic
Coefficient of Expansion, 70 – 200°F, 10-6 in/in •°F........ 7.3
21 – 93°C, µm/m• °C............ 13.1
Thermal Conductivity, Btu • in/ft2•h•°F ........................... 550
W/m• °C.......................................... 79.3
Electrical Resistivity, ohm• circ mil/ft..................................51
µΩ•m..............................................0.085

TYPICAL MECHANICAL PROPERTIES
(Annealed)
Tensile Strength, ksi.............................................................. 58.5
MPa............................................................ 403
Yield Strength (0.2% Offset), ksi...........................................15
MPa..................................... 103
Elongation, % ..............................................................................50

Mechanical properties of grade NICKEL 201 UNS N02201

Proof strength Rp0.2 (MPa)	Tensile strength Rm (MPa)	Impact energy KV (J)	Elongation at fracture A (%)	Reduction in cross section on fracture Z (%)	As-Heat-Treated Condition	Brinell hardness (HBW)
131 (≥)	536 (≥)	13	24	13	Solution and Aging, Annealing, Ausaging, Q+T,etc	324

Physical properties of grade NICKEL 201 UNS N02201

Property	Density kg/dm3	Temperature T °C/F	Specific heat J / kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2	Expansion rate
938 (≥)	115 (≥)	11	21	34	Solution and Aging, Annealing, Ausaging, Q+T,etc	113
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0) N/mm2	Creep rupture strength (10000h) (Rp1,0) N/mm2
792	812	113