Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.030 | ||
Si | - | 1.00 | ||
Mn | - | 2.00 | ||
P | - | 0.035 | ||
S | - | 0.030 | ||
Ni | 8.00 | 12.00 | ||
Cr | 18.00 | 20.00 |
00Cr19Ni10 Stainless and heat resisting steels.
GB 13296 (2007) Seamless stainless steel tubes for boiler and heat exchanger
Austenitic steel; Allowable stress data source: GB 150.2:2011.
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
618 (≥) | 486 (≥) | 34 | 32 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
554 (≥) | 199 (≥) | 43 | 33 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
263 | 523 | 925 |
We can customize the production of 00Cr19Ni10 grade, contact us for the best solution.