Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.40 | 0.50 | ||
| Si | 2.70 | 3.30 | ||
| Mn | - | 0.80 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 8.00 | 10.00 | ||
| Mo | - | - | ||
| Ni | - | 0.60 |
Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 858 (≥) | 995 (≥) | 23 | 14 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 241 (≥) | 554 (≥) | 41 | 41 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 141 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 261 | 889 | 558 |
We can customize the production of X45CrSi9-3 grade, contact us for the best solution.