Austenitic and Martensitic Stainless Steel Bars, Billets, and Forgings for Liquid Metal Cooled Reactor Core Components
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Mn | - | 2.00 | ||
| Si | - | 1.00 | ||
| P | - | 0.045 | ||
| S | - | 0.03 | ||
| Cr | 11.50 | 13.50 | ||
| Ni | 14.00 | 16.00 |
Austenitic and Martensitic Stainless Steel Bars, Billets, and Forgings for Liquid Metal Cooled Reactor Core Components
Standard Withdrawn
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 547 (≥) | 749 (≥) | 41 | 33 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 661 (≥) | 598 (≥) | 42 | 32 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 243 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 122 | 684 | 755 |
We can customize the production of A 831 S38660 grade, contact us for the best solution.
–sales@specificsteel.com