Electric-Fusion-Welded Austenitic Chromium-Nickel Stainless Steel Pipe for High-Temperature Service and General Applications
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.018 | ||
| Mn | - | 2.00 | ||
| Si | 3.70 | 4.30 | ||
| P | - | 0.02 | ||
| S | - | 0.02 | ||
| Cr | 17.00 | 18.50 | ||
| Ni | 14.00 | 15.50 | ||
| Mo | - | 0.20 |
Electric-Fusion-Welded Austenitic Chromium-Nickel Stainless Steel Pipe for High-Temperature Service and General Applications
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 957 (≥) | 987 (≥) | 42 | 11 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 114 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 392 (≥) | 381 (≥) | 34 | 42 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 937 | 382 | 577 |
We can customize the production of A 358 S30600 grade, contact us for the best solution.
–sales@specificsteel.com