Specification for nickel-silicon-chromium-molybdenum-vanadium steel (vacuum arc remelted) billets, bars, forgings and parts (1900-2100 MPa: limiting ruling section 75 mm)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.07 | ||
| Si | - | 0.60 | ||
| Mn | - | 1.00 | ||
| P | - | 0.035 | ||
| S | - | 0.025 | ||
| Cr | 13.20 | 14.70 | ||
| Ni | 5.00 | 5.80 | ||
| Mo | 1.20 | 2.00 | ||
| Nb | 0.10 | 0.40 | ||
| Cu | 1.20 | 2.00 |
Specification for nickel-silicon-chromium-molybdenum-vanadium steel (vacuum arc remelted) billets, bars, forgings and parts (1900-2100 MPa: limiting ruling section 75 mm)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 454 (≥) | 876 (≥) | 21 | 13 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 888 (≥) | 725 (≥) | 33 | 11 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 657 | 791 | 689 |
We can customize the production of 2S.155 grade, contact us for the best solution.