Classification and designation for superalloys and high temperature intermetallic materials
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.06 | ||
Cr | 18.0 | 21.0 | ||
Mo | 3.70 | 4.30 | ||
Ni | 40.0 | 44.0 | ||
W | 1.80 | 2.20 | ||
Al | 0.35 | 0.75 | ||
Ti | 1.80 | 2.20 | ||
Si | - | 0.60 | ||
Mn | - | 0.50 | ||
P | - | 0.020 | ||
S | - | 0.015 | ||
B | - | 0.015 | ||
Ce | - | 0.02 | ||
Zr | - | 0.05 |
GH2018
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
814 (≥) | 254 (≥) | 13 | 22 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 233 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
169 (≥) | 192 (≥) | 42 | 32 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 323 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
289 | 875 | 423 |
We can customize the production of GH2018 grade, contact us for the best solution.