HR404

HR404 Stainless Steels to BS HR 404 (1973)

HR404 - Specification & Application

• BS HR 404 (1973) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)
• BS 2HR 404 (2011) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Chemical composition(wt.%) of HR404 grade: to BS HR 404 (1973)

HR404 - Detail

Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Mechanical properties of grade HR404 BS HR 404 (1973)

Proof strength Rp0.2 (MPa)	Tensile strength Rm (MPa)	Impact energy KV (J)	Elongation at fracture A (%)	Reduction in cross section on fracture Z (%)	As-Heat-Treated Condition	Brinell hardness (HBW)
444 (≥)	366 (≥)	24	24	33	Solution and Aging, Annealing, Ausaging, Q+T,etc	441

Physical properties of grade HR404 BS HR 404 (1973)

Property	Density kg/dm3	Temperature T °C/F	Specific heat J / kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2	Expansion rate
832 (≥)	163 (≥)	23	12	24	Solution and Aging, Annealing, Ausaging, Q+T,etc	222
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0) N/mm2	Creep rupture strength (10000h) (Rp1,0) N/mm2
469	625	711