0Cr18Ni12Mo2Cu2 stainless steel corrosion resistance, resistance to corrosion resistance is better than 0Cr17Ni12Mo2. 0Cr18Ni12Mo2Cu2 stainless steel used in the sulphuric acid resistant material.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.030 | ||
| Ni | 10.00 | 14.50 | ||
| Cr | 17.00 | 19.00 | ||
| Mo | 1.20 | 2.75 | ||
| Cu | 1.00 | 2.50 |
0Cr18Ni12Mo2Cu2
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 656 (≥) | 247 (≥) | 43 | 31 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 423 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 744 (≥) | 566 (≥) | 12 | 44 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 331 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 433 | 991 | 966 |
We can customize the production of 0Cr18Ni12Mo2Cu2 grade, contact us for the best solution.