Stainless steel billets and bars intended only for forging
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.25 | ||
| Si | 1.50 | 3.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.03 | ||
| Cr | 23.0 | 26.0 | ||
| Ni | 19.0 | 22.0 |
Stainless and heat resisting steels
Stainless steel billets and bars intended only for forging,Material is supplied as rolled or as forged.
A 270 314
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 926 (≥) | 114 (≥) | 41 | 31 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 436 (≥) | 569 (≥) | 32 | 33 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 744 | 387 | 751 |
We can customize the production of A 314 314 grade, contact us for the best solution.