Cold-Work Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.95 | 1.05 | ||
| Si | 0.10 | 0.50 | ||
| Mn | 1.80 | 2.20 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 0.90 | 1.20 | ||
| Mo | 0.90 | 1.40 | ||
| V | - | - | ||
| W | - | - | ||
| Ni＋Cu | - | 0.75 |
Cold-Work Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 922 (≥) | 312 (≥) | 32 | 22 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 412 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 963 (≥) | 581 (≥) | 12 | 33 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 434 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 421 | 375 | 971 |
We can customize the production of A4 grade, contact us for the best solution.