Co-Cr-Ni-W alloy
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.05 | 0.15 | ||
| Mn | 1.00 | 2.00 | ||
| P | - | 0.40 | ||
| S | - | 0.03 | ||
| Si | - | 0.40 | ||
| Cr | 19.00 | 21.00 | ||
| Ni | 9.00 | 11.00 | ||
| Co | - | Bal | ||
| Fe | - | 3.0 | ||
| W | 14.00 | 16.00 |
HS25 HS-25 L605 R30605 Haynes-25 has an excellent temperature strength and oxidation resistance to 2000 ºF. Haynes 25™ is hot formable between 1900 ºF- 2300 ºF. Also known as Alloy L605, it is better to cold-work Haynes 25™ for bending, spinning and drawing the components.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 183 (≥) | 893 (≥) | 11 | 12 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 625 (≥) | 174 (≥) | 44 | 34 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 638 | 913 | 732 |
We can customize the production of R30605 grade, contact us for the best solution.