Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.06 | 0.12 | ||
| Si | - | 0.80 | ||
| Mn | - | 0.70 | ||
| P | - | 0.030 | ||
| S | - | 0.020 | ||
| Cr | 20.00 | 23.00 | ||
| Ni | 35.00 | 39.00 | ||
| Mo | - | - | ||
| Al | - | 0.50 | ||
| Ti | 0.70 | 1.20 | ||
| Fe | - | - | ||
| W | 2.80 | 3.50 | ||
| Ce | - | 0.05 |
Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 596 (≥) | 778 (≥) | 21 | 31 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 991 (≥) | 944 (≥) | 23 | 11 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 971 | 173 | 668 |
We can customize the production of XH38BT grade, contact us for the best solution.